| Properties |
Test Method Based On |
Units & Conditions |
Typical Values (2) |
| MooneyViscosityML1+4 |
ASTM |
MU@100°C |
80.8 |
| MooneyViscosityML1+8 |
D1646 |
MU@100°C |
80.6 |
| MRI |
|
Seconds |
3.1 |
| MooneyScorch |
|
|
|
| Mini mumViscosity |
ASTM |
MU@125°C |
62.2 |
| Timeto1ptrise |
D1646 |
Minutes |
7.8 |
| Timrto5ptrise |
|
Minutes |
26.6 |
| MDR Rhemeter |
|
180°C;Arc0.5°C |
|
| ML(Minimumtorque) |
ASTM |
dN.m |
2.8 |
| MH(Maximumtorque) |
D5289 |
dN.m |
10.7 |
| MH-ML(AT) |
|
dN.m |
7.8 |
| Tc2(timeto2torqueunitincrease) |
|
Minutes |
7.0 |
| Tc10(timeto10%torqueincrease) |
|
Minutes |
3.5 |
| Tc50(timeto50%torqueincrease) |
|
Minutes |
12.1 |
| Tc90(timeto90%torqueincrease) |
|
Minutes |
24.6 |
| TensileStrength |
ASTM |
MPa |
12.5 |
| Elongation |
D412 |
% |
860 |
| 300%Modules |
|
MPa |
2.5 |
| Hardness, ShoreA |
ASTMD2240 |
ShoreA |
47 |
| TearStrength(Die-B) |
ASTM D624 |
KN/m |
34.9 |